Bayblend FR3000
Injection molding grade; easy-flow grade; Vicat/B 120 temperature = 97 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability.
Bayblend FR3005
Injection molding grade; easy-flow grade; Vicat/B 120 temperature = 95 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability.
Bayblend FR3005 HF
Injection molding grade; very easy-flow grade; Vicat/B 120 temperature = 96 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant.
Bayblend FR3010
Injection molding grade; increased heat resistance; Vicat/B 120 temperature = 110 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); improved chemical resistance and stress cracking behavior; successor to FR2010.
Bayblend FR3010 IF
Injection molding grade; increased heat resistance; Vicat/B 120 temperature = 108 °C; improved flammability; UL recognition 94 5VB (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); improved flow compared to FR3010.
Bayblend KU2-1514
High heat resistant injection molding grade; ball indentation temperature >=125 °C; Vicat/B 120 temperature = 136 °C; UL recognition 94 V-0 at 1.5 mm; suitable for supporting life components.
Bayblend KU2-1514 BBS073
High heat resistant injection molding grade; improved chemical resistance and stress cracking behavior compared to KU2-1514; ball indentation temperature >= 125 °C; Vicat/B 120 temperature = 136 °C; UL recognition 94 V-0 at 1.5 mm; antimony-, chlorine- and bromine-free flame retardant; suitable for supporting life components.
Bayblend T45 PG
General purpose injection molding grade; Vicat/B 120 temperature = 112 °C; for electroplating applications.
Bayblend T50 XF
Injection molding grade; Vicat/B 120 = 115 °C; excellent flow; good low temperature impact strength.
Bayblend T65
General purpose injection molding grade; Vicat/B 120 temperature = 120 °C; good low temperature impact strength.
Bayblend T65 HI
Grade with improved low-temperature impact strength and chemical resistance for automotive parts; also suitable for extrusion/extrusion blow molding and electroplating applications; Vicat/B 120 temperature = 120 °C.
Bayblend T65 XF
General purpose injection molding grade; Vicat/B 120 temperature = 120 °C; improved flowability compared to T65.
Bayblend T80 XG
Injection molding grade; Vicat/B 120 temperature = 127 °C; excellent flow; optimized surface quality for metallization (steam treatment).
Bayblend T85
General purpose injection molding grade; Vicat/B 120 temperature = 131°C; high impact and notched impact strength.
Bayblend T85 XF
General purpose injection molding grade; Vicat/B 120 temperature = 130°C; better flow than T85.
Bayblend T88 GF-10
Injection molding grade; 10 % GF; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 5100 MPa; Vicat/B 120 = 134 °C.
Bayblend T88 GF-20
Injection molding grade; 20 % GF; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 7500 MPa; Vicat/B 120 = 130 °C.
Bayblend T88 GF-30
Injection molding grade; 31 % GF; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 10000 MPa; Vicat/B 120 = 134 °C
Bayblend® is the trade name used by Bayer MaterialScience for its product line of amorphous, thermoplastic polymer blends based on polycarbonate and ABS. The blend technology employed supplies products with an attractive combination of mechanical, thermal and rheological properties. Particular mention should be made of Bayblend®`s high heat resistance (between that of ABS and PC), its high impact and notched impact strength, and its high stiffness and dimensional stability.